Conveyor belts are widely used, of which the demand for heat-resistant conveyor belts is relatively large, but heat-resistant conveyor belts are a consumable, which will wear and tear if used for a long time. A wire rope conveyor belt manufacturer will introduce it to you.

　　1. 输送带开裂:主要受空间尺寸的限制，输送带弯曲次数较大;接头硫化由于多种原因引起的硫化有两种以上。导槽衬板与胶带间隙不适当，造成异常磨损，或在间隙内嵌异物，造成异常磨损或划伤。导槽处物料流量与输送带速度不一致，下降较大，加速了橡胶表面的磨损。辊筒损坏，导致胶带异常磨损或划伤。皮带打滑，也会造成胶带的异常磨损。

　　1. Conveyor belt cracking: mainly limited by space size, conveyor belt bending times are larger; joint vulcanization due to a variety of reasons caused by more than two kinds of vulcanization. The gap between guide groove liner and tape is inappropriate, resulting in abnormal wear or foreign body embedded in the gap, resulting in abnormal wear or scratch. The material flow rate at the guide groove is not consistent with the speed of the conveyor belt, which decreases greatly and accelerates the wear of the rubber surface. Roller damage, resulting in abnormal wear or scratch of tape. The slippage of belt will also cause abnormal wear and tear of belt.

　　2. 耐高温输送带纵向撕裂:主要是由于振动和冲击导致紧固件松动脱落，导致落煤管衬板和导板脱落。外来物质混合在材料中，材料是硬的、硬的、有边的、有边的。

　　2. Longitudinal tearing of high temperature resistant conveyor belt: It is mainly due to vibration and impact that the fasteners loose and fall off, leading to the falling coal pipe liner and guide plate fall off. Foreign materials are mixed in materials, which are hard, hard, edged and edged.

　　3、输送带裂纹:主要是由于输送带的老化，输送带运行时间长，因为老化往往导致输送带开裂。另外可能选择的输送带也是不合适的。

　　3. Conveyor belt cracks: mainly due to the aging of conveyor belt, conveyor belt running time is long, because aging often leads to conveyor belt cracking. In addition, the possible choice of conveyor belt is also inappropriate.

　　通过对钢丝绳输送带生产厂家的介绍，得出了输送带耐热的效果?你知道有什么损失吗?希望我们的介绍能对您有帮助

　　By introducing the manufacturer of wire rope conveyor belt, the heat-resistant effect of the conveyor belt is obtained. Do you know what the loss is? I hope our introduction will be helpful to you.